Silica refractory product |
Silica refractory product is used in various coke oven, glass kiln, hot-air furnace and gas furnace. |
|
|
Performance index |
Item |
Index |
GZ-96 |
GZ-95 |
GZ-94 |
¦Ø£¨SiO2£© % ¡Ý |
96 |
95 |
94 |
¦Ø£¨Fe2O3£© % ¡Ü |
1.0 |
1.2 |
1.4 |
Apparent porosity % |
22. |
Cold crushing strength /MPa ¡Ý |
weight£¼20kg |
35 |
weight¡Ý20kg |
30 |
0.20MPa Refractoriness under load ¡Ý |
1660 |
1650 |
1640(silica as binder1620) |
True density
g/cm3 ¡Ü |
2.34 |
2.35 |
|
|
Silica brick for blast furnace |
Performance index |
Item |
Index |
Wall brick for arch ceiling kiln |
Checker brick |
SiO2 %
No less than |
95 |
Cold crushing strength MPa
No less than |
35 |
30 |
Apparent porosity % No more than |
22. |
23 |
Creep rate£¬%£¨0.2MPa,1550¡æ£¬50h£©No more than |
0.8 |
True density g/cm3
No more than |
2.35 |
Thermal expansion coefficient£¨1000 ¡æ£©%
No more than |
1.26 |
Residual quartz£¬% |
provide data |
|
|
Silica brick for glass kiln |
Performance index |
Item |
Index |
BG-96A |
BG-96B |
BG-95A |
BG-95B |
SiO2 %
No less than |
96 |
96 |
95 |
95 |
Fe2O3 %
No more than |
0.8 |
1.0 |
1.2 |
1.2 |
Apparent porosity %
No more than |
22 |
Melting index
No more than |
weight£¼20kg |
0.5 |
¡ª |
0.7 |
¡ª |
weight¡Ý20kg |
0.6 |
¡ª |
0.7 |
¡ª |
0.20MPa Refractoriness under load¡æ
No less than |
1680 |
1670 |
1660 |
1650 |
True density g/cm3
No more than |
2.34 |
2.35 |
Cold crushing strength MPa No less than |
weight£¼20kg |
35 |
weight¡Ý20kg |
30 |
|
|
High-quality silica brick for glass kiln |
Performance index |
Item |
Index |
XBG-96 |
ZBG-96 |
DBG-95 |
SiO2 % ¡Ý |
96 |
96 |
96 |
Fe2O3 % ¡Ü |
0.9 |
0.9 |
1.0 |
Apparent porosity % ¡Ü |
22 |
23 |
24 |
Melting index£¬% ¡Ü |
0.5 |
0.5 |
0.6 |
Reheating linear change % 1450 ¡æ£¬2h ¡Ü |
0.3 |
0.3 |
0.3 |
0.20MPa Refractoriness under load¡æ ¡Ý |
1680 |
1680 |
1670 |
True density g/cm3 ¡Ü |
2.34 |
2..34 |
2.35 |
Cold crushing strength MPa ¡Ý |
35 |
30 |
30 |
weight kg |
¡Ü15 |
£¾15¡ª¡Ü25 |
£¾25¡ª¡Ü40 |
|
|
Silica brick for coke oven |
Performance index |
Item |
Index |
Furnace bottom, furnace wall |
Others |
SiO2 %
No less than |
94 |
Cold crushing strength MPa
No less than |
30 |
25 |
Apparent porosity %
No more than |
22. |
24 |
0.20MPa Refractoriness under load ¡æ
No less than |
1650(silica as binder1620) |
Reheating linear change % 1450 ¡æ£¬2h |
0¡ª+0.2 |
True density g/cm3
No more than |
2.34 |
2.35 |
Thermal expansion coefficient£¨1000 ¡æ£©%
No more than |
1.28 |
1.30 |
|
|
|